聚脂树脂 玻璃纤维带
浸胶 涤纶/玻璃纤维交织带
环氧树脂 涤纶收缩带
Woven Tape Impregnated with Polyester or Epoxy Resin
 |
我公司专业生产海鹰牌玻璃纤维、涤纶纤维、涤纶纤维/玻璃纤维交织、树脂预浸绑扎带.此类绑扎带经过织造加工后再浸渍树脂，制成半固化之卷装产品，广泛用于电机、变压器、互感器、电抗器铁芯的绑扎，避雷器的阀片绑扎，电机的转子绑扎，是变压器、互感器、电抗器、避雷器、电机制造生产厂家首选的优良绝缘材料。 Our company specializes in manufacturing of E-glass fiber tape、polyester filament tape、polyester filament and E-glass fiber interlace tape impregnated with polyester resin or epoxy resin.The tapes above mentioned are woven with yarns then impregnated with resins into semi-curing products. They are widely used as banding materials in the fields of transformer、reactor and lightning arrester, becoming good insulating matetrials for manufaturers. |
性能 Property：
型 号 Type |
HY 750 |
HY 740-1 HY 740-2 HY 740-3 |
HY 741-1 HY 741-2 HY 741-3 |
耐热等级 Thermal class |
H |
F |
F |
挥发物含量 Volatile content |
≤4% |
≤6% |
≤6% |
树脂含量 Loss of weight at calcination |
29%±2% |
30%±2% |
30%±2% |
可溶性树脂含量 Soluble resin content |
≥90% |
≥90% |
≥90% |
固化前的抗拉强度 Tensile strength before curing |
HY 740-1 |
||
最大绑扎力 Maximum pull while banding |
HY 740-1 |
||
 |
 |
规格 Specification:
| 厚度 Thickness(mm) | 宽度 Width(mm) | 长度 Length(M/pancake) |
| 0.14、0.20、0.30 | 10、15、20、25、30、50 | 100、150、200 |
根据需要可提供特殊规格和特殊卷长(如筒状)
Special specification and package are availabe upon request,(such as spool)
固化条件 Curing cycles:
| 温度 Temperature(℃) | 160 | 150 | 135 | 120 | 115 |
| 时间(小时) Time(hour) | 4 | 5 | 8 | 16 | 24 |
上述时间不包括工件加热所需时间
The above times do not include the time for the workpiece to reach the curing temperature.
贮存 Storage stabiliy:
贮存温度 Storage temperture ℃ |
0℃~20℃ | 21℃~30℃ |
| 时间(天) Time(day) | 60 | 45 |
 |
 |
|